| 牌号简介 About |
|---|
| Clearflex® CL D0是一种线性低密度聚乙烯，含有抗氧化剂，以极低密度（VLDPE）为特征。这种树脂是用专有技术生产的。用Clearflex® CL D0制造的拉伸膜具有高拉伸性、高清晰度和很高的粘着力。主要用途Clearflex® CL D0推荐用作拉伸膜中的粘接剂，但也可用于需要柔软触感和柔韧性的应用，以提高抗冲击性，当用作与其他聚烯烃混合时，使用或不使用矿物填料。 Clearflex CL D0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). This resin is produced with a proprietary technology. Stretch films manufactured with Clearflex CL D0 have high stretchability, outstanding clarity and very high constancy in cling effect. Main Application Clearflex CL D0 is recommended as cling agent in stretch film but it is also used for applications in which soft touch and flexibility are required, for the improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers. |
产品描述 Product Description
用途：薄膜;柔软触感应用;拉伸缠绕;混合;
性能特点： 拉伸性能好; 抗氧化; 柔软性好; 透光性好; 食品接触; 韧性好; 低密度; 高粘接度; Good Clarity,Good flexibility,Food contact compliance,Inoxidizability,Good Tensile Strength,Low density,High adhesion degrees,Soft
填料：矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 Frictional coefficient |
|||
|
与自身 - 动态，铸造薄膜 With oneself - dynamic, casting thin films |
注册或登录后
所有资料免费
|
ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
注册或登录后
所有资料免费
|
||
|
拉伸模量 Tensile modulus |
注册或登录后
所有资料免费
|
ISO 527-3 | |
|
1% 正割，MD，铸造薄膜 1% secant, MD, cast thin film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
1% 正割，TD，铸造薄膜 1% secant, TD, cast thin film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ISO 527-3 | |
|
MD，屈服，吹塑薄膜 MD, yield, blow molded film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
TD，屈服，吹塑薄膜 TD, yield, blow molded film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ISO 527-3 | |
|
MD，断裂，吹塑薄膜 MD, fracture, blow molded film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
TD，断裂，吹塑薄膜 TD, fracture, blow molded film |
注册或登录后
所有资料免费
|
MPa | ISO 527-3 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
ISO 527-3 | |
|
MD，断裂，挤塑薄膜 MD, fracture, extruded film |
注册或登录后
所有资料免费
|
% | ISO 527-3 |
|
TD，断裂，挤塑薄膜 TD, fracture, extruded film |
注册或登录后
所有资料免费
|
% | ISO 527-3 |
|
落锤冲击 Gardner Impact 2 |
注册或登录后
所有资料免费
|
||
|
铸造薄膜 Casting thin film 2 |
注册或登录后
所有资料免费
|
g | ISO 7765-1/A |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
注册或登录后
所有资料免费
|
ISO 6383-2 | |
|
MD MD |
注册或登录后
所有资料免费
|
kN/m | ISO 6383-2 |
|
TD TD |
注册或登录后
所有资料免费
|
kN/m | ISO 6383-2 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Brittle Temperature |
注册或登录后
所有资料免费
|
℃ | ASTM D746 |
|
维卡软化温度 Vicat Softening Temperature |
注册或登录后
所有资料免费
|
℃ | ISO 306/A |
|
熔融温度 Melting temperature |
注册或登录后
所有资料免费
|
℃ | 内部方法 |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
注册或登录后
所有资料免费
|
||
|
45°，铸造薄膜 45 °, cast thin film |
注册或登录后
所有资料免费
|
ASTM D2457 | |
|
雾度 Haze |
注册或登录后
所有资料免费
|
||
|
铸造薄膜 Casting thin film |
注册或登录后
所有资料免费
|
% | ISO 14782 |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
| 3 Cast Film |
|