牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种硬质、可着色、非吸湿性热塑性硫化弹性 体(TPV)。这种材料同时具有良好的物理性质和耐化学性,适用于广泛的领域。 这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型、挤出 成型、吹塑成型、热成型或真空成型设备上加工。这是一种聚烯烃基材料,可在生 产过程中进行回收利用。 A hard, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ASTM D792 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
13.0 | MPa | ASTM D412 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
13.0 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
7.10 | MPa | ASTM D412 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Brittle Temperature |
℃ | ASTM D746 | |
脆化温度 Brittle Temperature |
℃ | ISO 812 | |
相对温度指数 Relative temperature index |
|||
电气性能 ELECTRICAL |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.1 mm 1.1 mm |
℃ | UL 746 | |
1.6 mm 1.6 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 Change in Tensile Strength in Air |
|||
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(150℃,168 hr) Change in Tensile Strain at Break in Air(150℃,168 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,150℃,168 hr) Change in Durometer Hardness in Air (150 ℃, 168 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 Change in Shore Hardness in Air |
|||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
Change in Mass in Air(150℃,168 hr) Change in Mass in Air(150℃,168 hr) |
% | ASTM D573 | |
Change in Mass in Air(150℃,168 hr) Change in Mass in Air(150℃,168 hr) |
% | ISO 188 | |
拉伸强度的变化率 Change in Tensile Strength |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
拉伸强度的变化率 Change in Tensile Strength |
ISO 1817 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
极限伸长率的变化率 Change in Ultimate Elongation |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
断裂时拉伸应力变化 Change in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
邵氏硬度的变化率 Change rate of Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ASTM D471 | ||
邵氏硬度的变化率 Change rate of Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ISO 1817 | ||
质量变化率 Quality change rate |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
质量变化率 Quality change rate |
ISO 1817 | ||
23.0℃,168 hr,in Water 23.0℃,168 hr,in Water |
% | ISO 1817 | |
23.0℃,168 hr,in Sulfuric Acid,98% 23.0℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23.0℃,168 hr,in IRM 903 Oil 23.0℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Comparative Tracking Index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.6 mm 1.6 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
页岩气六年之约 壳牌与中石油或走到尽头?
2016-01-25 中石油、中石化近日分别晒出了自己最新打造出来的“国家级页岩气示范基地”,即涪陵页岩气田和长宁-威远页岩气区。我的地盘我做主,难得两大公司能自己玩转页岩气。但此时不禁又要问,当年信誓旦旦来四川闯页岩气的壳牌石油哪儿去了? 当初意气风发 壳牌石油不仅是最早来中国淘金的海外石油公司,也是最早进驻中国挑战页岩气的海外公司。2009年起,壳牌就牵手中石油,致力于页岩气项目的合作。于是,中国的第一个页岩气项目“富顺-永川页岩气项目”就这 |
页岩气六年之约 壳牌与中石油或走到尽头? 中国石油、中国石化近日各自晒出了自身全新打造出出去的“国家级别页岩气示范性产业基地”,即涪陵页岩气田和长宁区-威远页岩气区。我的地盘作主,难能可贵两大企业能自身轻松玩页岩气。但这时禁不住又要问,当初言而有信来四川闯页岩气的壳牌原油哪里来到? 当时斗志昂扬 壳牌原油不但是最开始来中国挖金的国外石油公司,也是最开始入驻中国挑戰页岩气的海外公司。2009年起,壳牌就牵手上原油,着眼于页岩气项目的协作。因此,中国的第一个页岩气项目“富顺-重庆永川页岩气项目”就那么问世了。该项目曾一度被当作是中国页岩气产业发展规划的榜样。在项目实行前期,斗志昂扬的壳牌高层住宅放话,假如项目成功,每一年将在中国页岩气项目投资10亿美金。 六年時间过去,中国石油、中国石化地地道道的页岩气示范性产业基地都创建起来了,但富顺-重庆永川页岩气协作项目进度却自始至终不冷不热。在2014外国媒体曾一度报导说壳牌要撤出或减缩富顺-重庆永川页岩气项目项目投资,壳牌对于此事也仅仅表明该地域地质学构造繁琐、周边人口密集,有众多不好项目进行的要素。但另外,壳牌也未声明要舍弃富顺-重庆永川页岩气项目。 环顾全世界看,壳牌的页岩气项目进度也并不是一帆风顺。有组织曾在2013年做了调研,尽管北美地区的页岩气开发设计以颠覆性的经营规模在发展趋势,可是以壳牌、BP为意味着的国际石油大企业却并沒有在北美地区页岩气项目上得到是多少盈利,从北美地区页岩气项目获利的绝大多数是一些中小型石油公司。此外在2015年初,壳牌还放弃了在巴西固守了六年的页岩气项目,和这一可采储量390万亿元立方英寸的黑富美提出分手,可能壳牌也是下了绝情的。这时又得问了,和中国石油十指紧扣取得成功的壳牌如今还能在四川坚持不懈多长时间呢? 壳牌大哥有话说 2016年1月20号,壳牌原油对2015年自身的考试成绩估了一次分,2015年的第四个一季度的营业收入可能在16-19亿美金中间,全年度营业收入在 104-107亿美金中间,全年度营业收入对比2014年降低超出52%。在那么艰辛的状况下,壳牌仍在2020年4月忍痛割爱豪掷700亿美金回收BG(美国燃气集团公司),花这么多钱,别的地区必然也是减少了许多项目投资。 壳牌CEO Ben van Beurden在20号发布的申明中尤其提及,从2014年至2015年,壳牌早已甩货了使用价值超出200亿美金的废铜烂铁,远超2014年初设置的 150亿美金。假如当今的并购业务成功,2016-2018年还将甩货300亿美金的财产。除开再次大甩卖,壳牌早已决策放开手这些项目投资时间长、收益低的上下游业务流程,例如阿拉斯加犬的勘查业务流程、Carmon Creek 油砂项目、在好几个我国进行的页岩项目。好几个我国的页岩项目!!!他们非常容易令人想到到壳牌的四川页岩气项目,来看壳牌和中国石油这一段页岩情早已是摇摇欲坠了。 尽管中国石油以前还怄气说过“我一个人走,没事儿,总之因为我早已把握了开发设计页岩气的方式了”。但从2015年11月,BP企业又来四川第三者插足页岩气项目一事看,中国石油对壳牌也是丧失自信心了。 在中国销售市场混在100很多年,壳牌也算作知名儿的中国通了。除开如今消沉的页岩项目,在中国的中下游业务流程确是很取得成功的,壳牌不但是中国较大 的国际性润滑脂经销商,并且在全国各地还有着1000好几个加气站。饱经竞技场的壳牌还是不可以彻底认清石油化工行业的方式,更别说阴差阳错入了原油这条道的平常人。和富顺-永安页岩气项目相关的游戏玩家,尤其要警醒了,过好多个礼拜和BG的合拼进行之后,壳牌的10000裁人大行动就需要开始了! 来源于:页面 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |