| 牌号简介 About |
|---|
| NANCAR® 4155J是一种高丙烯腈-丁二烯共聚物，具有优异的耐油性。它在低温下聚合，并含有足够的抗氧化剂，以满足正常老化条件。它具有固化速度快、模具结垢小、回弹性能好等特点。它在需要流动和编织的化合物中具有良好的加工特性，在高硬度化合物中尤其有价值。NANCAR® 4155J提供良好的加工和建筑定位。建议用于模制品、摩擦材料和类似用途。 NANCAR® 4155J is a high acrylonitrile butadiene copolymer with excellent oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has fast curing rate, low mold fouling and superior resilience properties. It has good processing characteristics in compounds where flow and knitting are desired and is especially valuable in high durometer compounds. NANCAR® 4155J provides good processing and building tack. It is suggeste for use in molded goods, friction stock and similar applications. |
产品描述 Product Description
用途：铸模/模具/工具;
性能特点： 耐油; 抗氧化; 共聚物; 有弹性; 易流动; 汽相固化; 易加工; Excellent Processability,Good liquidity,Steam Cure,Inoxidizability,Elastic,Copolymer,Grease resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.998 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
ASTM D1646 | ||
|
ML 1+4，100℃ ML 1+4，100℃ |
55 | MU | ASTM D1646 |
|
ML 1+4，100℃ ML 1+4，100℃ 2 |
75 | MU | ASTM D1646 |
|
丙烯腈含量（Bound） Acrylonitrile content (Bound) |
41.0 | % | 内部方法 |
|
Stabilizer Stabilizer |
Non-staining | ||
|
可溶性 solubility |
|||
|
in MEK in MEK |
% | ||
|
粘度 viscosity |
ASTM D1646 | ||
|
最低限度 Minimum limit |
ASTM D1646 | ||
|
Minutes to 35 points rise，t35 Minutes to 35 points rise，t35 |
min | ASTM D1646 | |
|
Minutes to 5 points rise，t5 Minutes to 5 points rise，t5 |
min | ASTM D1646 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 3 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 4 |
ASTM D2240 | ||
|
邵氏 A，5 秒 Shore A, 5 seconds 5 |
ASTM D2240 | ||
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
300% 应变 300% strain 3 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 4 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服 yield 3 |
MPa | ASTM D412 | |
|
屈服 yield 4 |
MPa | ASTM D412 | |
|
屈服 yield 5 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂 fracture 3 |
% | ASTM D412 | |
|
断裂 fracture 4 |
% | ASTM D412 | |
|
断裂 fracture 5 |
% | ASTM D412 | |
|
撕裂强度 tear strength 6 , 4 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation 5 |
|||
|
100℃，70 hr 100℃，70 hr 5 |
% | ASTM D395 | |
|
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 Change in Tensile Strength in Air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air 7 |
|||
|
100℃，70 hr 100℃，70 hr 7 |
% | ASTM D573 | |
|
空气中硬度计硬度的变化率 Change in Durometer Hardness in Air 7 |
|||
|
邵氏 A，100℃，70 hr Shore A, 100 ℃, 70 hr 7 |
ASTM D573 | ||
|
拉伸强度的变化率 Change in Tensile Strength 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
极限伸长率的变化率 Change in Ultimate Elongation 7 |
ASTM D471 | ||
|
100℃，70 hr，在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
邵氏硬度的变化率 Change rate of Shore hardness 7 |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
|
支撐 A，100℃，70 hr，在IRM 903油中 Support A, 100 ℃, 70 hr, in IRM 903 oil |
ASTM D471 | ||
|
体积变化 Volume change 7 |
ASTM D471 | ||
|
100℃，70 hr，ASTM 标准油（1号） 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
|
100℃，70 hr，在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D5688 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Uncured |
| 3 CURED @150°C for 60 mins |
| 4 CURED @150°C for 40 mins |
| 5 CURED @150°C for 20 mins |
| 6 C 模具 |
| 7 CURED@150°C × 40 MINUTES |
|
【新闻资讯】查看全部
东曹公司机能性聚氨酯产品价风格整告诉
2017-04-18 各位经销商及客户： 感谢大家对东曹产品的厚爱和支持。 虽然弊司在进行一系列的降低成本，合理化措施改进的努力，但由于原材料，综合费用，物流成本上涨所造成的收支核算的恶化程度已超过极限，维持现有价格已变得异常困难。为稳定供应，须及时对价格实施调整。 1. 调整对象 HDI单体及HDI系列固化剂 聚碳酸酯二元醇PCD产品 TDI系列固化剂 2. 价格调整幅度 HDI单体 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付