牌号简介 About |
---|
20%玻璃纤维填充,超高流量聚醚酰亚胺(PEI)(TG 217degC),内部模具释放和平衡性能与流量和延性,符合ECO,UL94 V0清单 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.4314 | g/cm³ | ISO 1183 |
模具收缩率 Mold Shrinkage |
|||
MD MD |
0.3833 | % | |
TD TD |
0.4466 | % | |
吸湿性 Moisture Absorption |
|||
23℃/50% RH/24 hrs 23℃/50% RH/24 hrs |
0.05 | % | ISO 62 |
吸水率 Water Absorption |
|||
23℃, 24 hrs 23℃, 24 hrs |
0.136 | % | ASTM D570 |
比重 Specific Gravity |
ASTM D792 | ||
熔体体积流动速率 Melt Volume Rate |
|||
360℃, 2.16 kg 360℃, 2.16 kg |
cm³/10min | ISO 1133 | |
337℃, 6.7 kg 337℃, 6.7 kg |
cm³/10min | ISO 1133 | |
345℃, 10 kg 345℃, 10 kg |
cm³/10min | ISO 1133 | |
熔体质量流动速率 Melt Flow Rate |
|||
360℃, 2.16 kg 360℃, 2.16 kg |
g/10min | ASTM D1238 | |
337℃, 6.7 kg 337℃, 6.7 kg |
g/10min | ASTM D1238 | |
345℃, 10 kg 345℃, 10 kg |
g/10min | ASTM D1238 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲应力 Flexural Stress |
|||
屈服, 1.3 mm/min, 50 mm跨度 yld, 1.3 mm/min, 50 mm span |
MPa | ASTM D790 | |
断裂, 1.3 mm/min, 50 mm跨度 brk, 1.3 mm/min, 50 mm span |
MPa | ASTM D790 | |
屈服, 2 mm/min yld, 2 mm/min |
MPa | ISO 178 | |
断裂, 2 mm/min brk, 2 mm/min |
MPa | ISO 178 | |
弯曲模量 Flexural Modulus |
|||
1.3 mm/min, 50 mm跨度 1.3 mm/min, 50 mm span |
MPa | ASTM D790 | |
2 mm/min 2 mm/min |
MPa | ASTM D790 | |
拉伸应力 Tensile Stress |
|||
断裂, Type I, 5 mm/min brk, Type I, 5 mm/min |
MPa | ASTM D638 | |
断裂, 5 mm/min brk, 5 mm/min |
MPa | ISO 527 | |
拉伸模量 Tensile Modulus |
|||
5 mm/min 5 mm/min |
MPa | ASTM D638 | |
1 mm/min 1 mm/min |
MPa | ISO 527 | |
拉伸应变 Tensile Strain |
|||
断裂, Type I, 5 mm/min brk, Type I, 5 mm/min |
% | ASTM D638 | |
断裂, 5 mm/min brk, 5 mm/min |
% | ISO 527 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
80*10*4 +23°C 80*10*4 +23°C |
KJ/m² | ISO 180/1A | |
简支梁缺口冲击强度 Charpy notched Impact strength |
|||
23℃,V形缺口 80*10*4 sp=62mm 23°C, V-notch Edgew 80*10*4 sp=62mm |
kJ/m² | ISO 179/1eA | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
80*10*4 +23°C 80*10*4 +23°C |
KJ/m² | ISO 180/1U | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃ 80*10*4 sp=62mm 23℃ 80*10*4 sp=62mm |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.82 MPa, 3.2 mm, 未退火 1.82 MPa, 3.2 mm, unannealed |
℃ | ASTM D648 | |
1.82 MPa, 6.4 mm, 未退火 1.82 MPa, 6.4 mm, unannealed |
℃ | ASTM D648 | |
0.45 MPa, 3.2 mm, 未退火 0.45 MPa, 3.2 mm, unannealed |
℃ | ASTM D648 | |
0.45 MPa, 6.4 mm, 未退火 0.45 MPa, 6.4 mm, unannealed |
℃ | ASTM D648 | |
1.8 MPa Flatw 80*10*4 sp=64mm 1.8 MPa Flatw 80*10*4 sp=64mm |
℃ | ASTM D648 | |
0.45 MPa Flatw 80*10*4 sp=64mm 0.45 MPa Flatw 80*10*4 sp=64mm |
℃ | ASTM D648 | |
维卡软化点 vicat softening point |
|||
B/50 B/50 |
℃ | ASTM D-1525 | |
B/120 B/120 |
℃ | ASTM D-1525 | |
B/50 B/50 |
℃ | ISO 306 | |
B/120 B/120 |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-40℃-150℃ MD:-40℃-150℃ |
cm/cm/℃ | ASTM E831 | |
TD:-40℃-150℃ TD:-40℃-150℃ |
cm/cm/℃ | ASTM E831 | |
MD:23℃-150℃ MD:23℃-150℃ |
cm/cm/℃ | ISO 11359-2 | |
TD:23℃-150℃ TD:23℃-150℃ |
cm/cm/℃ | ISO 11359-2 | |
相对温度指数 Relative Temp Index(RTI) |
|||
电气 elec |
℃ | UL746B | |
冲击 imp |
℃ | UL746B | |
强度 str |
℃ | UL746B | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
1.5-1.6 mm 1.5-1.6 mm |
UL 94 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 ![]()
塑料行业收购音讯频传 做大做强信心坚决
2016-06-21 进入6月份以来,塑料行业的收购事件可谓是消息频出,各大企业,或为实现资源整合、资源共享;或进行市场扩充、进军国际领域;或以收购为媒介,进而转战其他相关产业等等,纷纷斥巨资来达到收购的目的,这也表现出企业积极面对挑战的乐观心态与做大做强的决心。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |