| 牌号简介 About |
|---|
| LS化合物的设计使零件收缩（出模）和后固化操作与丁腈或类似弹性体相当。在大多数情况下，切换到LS化合物时不需要更改工具。NPC表示，无需进行后固化，即可获得具有良好压缩永久变形和老化特性的高拉伸值和模量值。FKHT是一种耐高温、低压缩永久变形的化合物。FKX是一种高粘度、高绿色强度、黑色碳氟化合物，适用于O型圈帘线和挤压型材的HAV和/或盐浴固化。 The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles. |
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.96 | g/cm³ | |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10，121℃ ML 1+10，121℃ |
70 | MU | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
70 | ||
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
11.7 | MPa | |
|
100% 应变 100% strain |
4.41 | MPa | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ||
|
压缩形变 Compression deformation 2 |
|||
|
200℃，22 hr 200℃，22 hr 2 |
% | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Plied discs |
|
【新闻资讯】查看全部
环保力度绝后令钛白粉市场虚无缥缈
2017-11-20 目前，国内钛白粉市场价格稳定，成交量较为平稳。其中，涂料市场表现相对较好，部分大型企业订单充足。据业内人士向瑞道透露，目前钛白粉市场成交量较前期没有明显变化，而在10月份涨价潮过后，成交价并没有实际的提升，依旧与前期价格相当。随着北方即将进入供暖季，部分地区将受到限产影响，但其影响如何尚未可知。 由于今年国家对环保督查加强了力度，环保督查不仅钛白粉企业受到影响，下游客户同样受到限产或停产的影响，导致今年国内市场供需两端同时出现变化。这种情况在往年从未出现过，因此钛白粉企业及 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付