| 牌号简介 About |
|---|
| 低烟、低毒、无卤、阻燃、硅烷交联化合物，用于所有类型电缆的低压绝缘和护套。这是一种低烟、阻燃的硅烷交联化合物，可作为热塑性塑料在高输出速率下加工，并在潮湿条件下固化后加工。接枝组分SX559与交联催化剂母粒CM540U混合，通常比例为97:3至95:5。该化合物具有良好的机械、电气和阻燃性能，以满足包括BS 7211在内的严格绝缘规范。该化合物还可用于需要高阻燃性的电缆的护套。 Low-smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for low voltage insulation and sheathing of all types of cable This is a low smoke, low fume, fire retardant silane crosslinkable compound which can be processed as a thermoplastic at high output rates and cured post processing by exposure to moisture. The graft component SX559 is mixed with a crosslinking catalyst masterbatch CM540U generally in the ratio 97:3 to 95:5 The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications including BS 7211. The compound can also be used for sheathing of cables requiring high fire retardance. |
产品描述 Product Description
用途：电缆护套;电线电缆应用;低压绝缘;阻燃绝缘;阻燃护套;
加工条件：挤出 Extrusion
性能特点： 可交联; 无卤; 低烟; 低VOC; 阻燃; 毒性低; Low smoke,Crosslinked,Halogen free,Flame Characteristics,Low toxicity,Low odor
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.49 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.5 | g/10min | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
14.0 | MPa | IEC 60811-501 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
170 | % | IEC 60811-501 |
|
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度的变化率 Change in Tensile Strength |
|||
|
135℃，168 hr 135℃，168 hr |
20 | % | IEC 60811-1-2 |
|
断裂时拉伸应力变化 Change in tensile stress during fracture |
|||
|
135℃，168 hr 135℃，168 hr |
% | IEC 60811-1-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
变形 deformation |
|||
|
100℃ 100℃ |
% | IEC 60811-3-1 | |
|
低温弯曲 Low temperature bending |
|||
|
-30℃ -30℃ |
IEC 60811-1-4 | ||
|
热固性 thermosetting 2 |
|||
|
负荷下伸长率：20 N/cm²，200℃ Elongation under load: 20 N/cm ²， 200 ℃ |
% | ||
|
冷却后最大永久伸长率 Maximum permanent elongation after cooling |
% | ||
|
|
℃ | ISO 4589-3 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
绝缘电阻常数 - Ki Insulation resistance constant - Ki |
|||
|
20℃ 20℃ |
ohms·cm | ||
|
90℃ 90℃ |
ohms·cm | ||
|
|
µS/cm | IEC 60754-2 | |
|
|
% | ASTM D2843 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
腐蚀性气体 Corrosive gases |
pH | IEC 60754-2 | |
|
Halogen Acid Gas Evolution Halogen Acid Gas Evolution |
% | IEC 60754-1 | |
|
|
|||
| 备注 |
|---|
| 2. Cure assessment by hot set test (forced cured at 80°C in water) |
|
【新闻资讯】查看全部
调查显示英国海域废弃塑料袋数量下降
2018-04-16 英国农业、渔业、林业和食品部下属的环境、渔业和水产科学中心近日发布公报说，经过长达25年的跟踪调查，研究人员发现英国海域海床存在的废弃塑料袋数量持续下降，这意味着采取有效措施可能有助应对海洋垃圾问题。 研究人员对1992年至2017年间这些海域的垃圾情况进行了深入分析。结果发现，北海、英吉利海峡、凯尔特海以及爱尔兰海的海床存在多种类型的垃圾。其中，几乎所有海域都存在塑料袋、塑料瓶以及与捕鱼相关废弃物等塑料制品。 研究人员表示，尽管塑料袋这类垃圾的数量有所下降 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付