Kepstan是一种高性能热塑性材料,以聚醚酮酮(PEKK)为基础,具有高度稳定的化学主链。它的固态半晶体结构提供了机械和热强度以及化学和耐火性的出色结合。KEPSTAN™ 8010C40是一种碳纤维增强化合物,基于8000系列的Kepstan树脂。该系列提供了最高的玻璃化转变温度和最高的结晶度,从而使不同系列的Kepstan-Pekk共聚物具有最佳的拉伸和压缩强度。KEPSTAN™ 8010C40是一种低流量等级,适用于挤压、压缩和注射成型。KEPSTAN™ 8010C40以颗粒形式提供,包装在20公斤的箱子中。 KEPSTAN™ is a high performance thermoplastic material, based on PolyEtherKetoneKetone (PEKK) highly stable chemical backbone. Its semi crystalline structure in solid state offers an outstanding combination of mechanical and thermal strength together with chemical and fire resistance. KEPSTAN™ 8010C40 is a carbon fiber reinforced compound, based on the 8000 series of KEPSTAN™ resins. This series offers the highest glass transition temperature and the highest crystallinity, leading to the best tensile and compression strengths among the different series of KEPSTAN™ PEKK copolymers. KEPSTAN™ 8010C40 is a low flow grade, suitable for extrusion, compression and injection molding. KEPSTAN™ 8010C40 is available in pellet form and is packaged in 20 kg boxes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.45 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
380℃,5 kg 380℃,5 kg |
18 | cm³/10min | ISO 1133 |
吸水率 Water Absorption |
|||
23℃,24hr,2.00 mm 23℃,24hr,2.00 mm |
0.10 | % | |
饱和,23℃ Saturation, 23 ℃ |
0.40 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃,注塑成型 23 ℃, injection molding |
30300 | MPa | |
125℃,注塑成型 125 ℃, injection molding |
MPa | ||
拉伸强度 tensile strength |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ||
125℃,注塑成型 125 ℃, injection molding |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
% | ||
断裂,125℃,注塑成型 Fracture, 125 ℃, injection molding |
% | ||
弯曲模量 Flexural Modulus |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
KJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
玻璃化转变温度 Glass transition temperature |
℃ | ||
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
2、5.1 mm/min |
3、20°C/min |
4、20°C/min, 2nd heating |
【新闻资讯】查看全部 ![]()
最新!国家下达重要通知 家居行业正式迎来复苏期?
2020-12-26 搜料网资讯: 前两个月受疫情影响,世界各类展会宣布停办或延期。 而就在五一前夕,原本已延期到6月举办的国际名家具展(东莞)展览会和深圳时尚家居设计周又突然宣布双双延期 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |