| 牌号简介 About |
|---|
| Solanyl C2002是一种适合挤压的端部化合物。Solanyl C2002可以在传统的挤压生产线上加工。Solanyl C2002是目前使用的可生物降解塑料的竞争性替代品，如PP、HIPS和PS，适用范围广泛。Solanyl C2002可与大多数生物聚酯或淀粉基塑料混合，以降低成本。Solanyl C2002具有自然的手感和外观。Solanyl C2002可生物降解，生物基或植物基含量大于60%。可使用Solanyl C2002的应用包括：消费品和包装农产品热成型应用、杯、盒和托盘、板材和片材基础应用，如管道挤压型材。 Solanyl ® C2002 is an end compound suitable for extrusion. Solanyl ® C2002 can be processed on conventional extrusion lines. Solanyl ® C2002 is a competitive alternative for currently used biodegradable plastics, like PP, HIPS & PS for a wide range of applications. Solanyl ® C2002 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl ® C2002 has a natural feel and look. Solanyl ® C2002 is biodegradable and has a biobased or plant based content of >60%. Applications in which Solanyl ® C2002 can be used are: Consumer goods & Packaging Agriculture products Thermoform applications Cups, boxes & trays Plates and sheets Groundwork applications like pipes Extruded profiles |
产品描述 Product Description
用途：杯子;包装;片材;型材;托盘;热成型应用;管道系统;农业应用;
加工条件：挤出 Extrusion
性能特点： 可回收; 可堆肥; 食品接触; 生物可降解; Renewable resources,Biodegradable,Food contact compliance,Compostable
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 到 1.30 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.70 到 0.80 | g/cm³ | ISO 60 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
170℃，2.16kg 170℃，2.16kg |
2.0 到 4.0 | g/10min | |
|
螺旋流动长度 Spiral flow length 2 |
15.0 到 30.0 | cm | |
|
收缩率 Shrinkage |
< 2.0 | % | ISO 294-4 |
|
含水量 water content |
内部方法 | ||
|
灰份含量 Ash Content |
% | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
注塑成型 injection molding |
MPa | ||
|
正割，注塑成型 Cutting, injection molding |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服，注塑成型 Yield, injection molding |
% | ||
|
断裂，注塑成型 Fracture, injection molding |
% | ||
|
弯曲模量 Flexural Modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
弯曲强度 Flexural Strength |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
拉伸模量 Tensile modulus |
|||
|
MD MD |
MPa | ||
|
TD TD |
MPa | ||
|
拉伸强度 tensile strength |
|||
|
注塑成型 injection molding |
MPa | ISO 527-2 | |
|
MD，断裂 MD, fracture |
MPa | ||
|
TD，断裂 TD, fracture |
MPa | ||
|
MD MD |
MPa | ||
|
TD TD |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，屈服 MD, yield |
% | ||
|
TD，屈服 TD, yield |
% | ||
|
MD，断裂 MD, fracture |
% | ||
|
TD，断裂 TD, fracture |
% | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Activity Water Activity |
内部方法 | ||
| 备注 |
|---|
| 2、模具温度: 25°C, 熔体温度: 170 到 190°C |
|
【新闻资讯】查看全部
星巴克全球的店铺将逐步中止运用一次性塑料吸管
2018-07-30 根据日本NHK电视台7月23日报道，为了缓解日本塑料制品造成的环境污染困境，许多企业纷纷开始采取相关措施。例如，美国的星巴克公司宣布，全球的店铺将逐步停止使用一次性塑料吸管，并用可降解材质的产品进行替换等。 日本的一些相关厂商也积极采取相应措施。其中，大型造纸厂商日本制纸公司开发出了一种可以取代塑料袋包装的炸土豆片、谷物食品等的纸。因为这种纸进行了一些特殊工序的加工，所以具备着一定的防水以及密封方面的功能，可以替代部分的食品包装。 日本制纸公司表示，由于上述 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付