| 牌号简介 About |
|---|
| TN2005是一种高分子量的乙烯-醋酸乙烯酯共聚物，具有优异的机械性能、透明度、高光泽和易加工性。此外，TN2005即使在低温和良好的密封性能下也具有灵活性。TN2005可作为制备具有优良热性能的温室薄膜的基础聚合物。有关农用薄膜应用和光稳定建议的更多详细信息，请联系Braskem代表。用途：热农用薄膜（温室覆盖）。无紫外线添加剂。-用于食品包装的吹塑薄膜单或共挤冷冻食品包装薄膜具有良好机械性能的高清晰度薄膜。 TN2005 is an Ethylene-Vinyl Acetate (EVA) copolymer with high molecular weight, excellent mechanical properties, transparency, high gloss and easy processability. Additionally, TN2005 has flexibility even at low temperatures and good sealing properties. TN2005 can be used as base polymer for the manufacture of greenhouse films with excellent thermal properties. More detailed information about agricultural film applications and light stabilization recommendations, please contact a Braskem representative. Additives Antioxidant Application: Thermal agricultural film (greenhouse coverage). No UV-additives. Blown film mono or co-extrusion for food packaging Films for frozen food packaging High clarity film with excellent mechanical properties. |
产品描述 Product Description
用途：薄膜;包装;食品包装;农业应用;
加工条件：薄膜挤出 Film extrusion
性能特点： 耐低温柔性; 抗氧化; 共聚物; 高分子量; 透光性好; 韧性好; 表面光泽度好; 易加工; Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,Inoxidizability,High molecular weight,Low temperature toughness,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.935 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.50 | g/10min | ASTM D1238 |
|
醋酸乙烯含量 Vinyl acetate content |
13.5 | wt% | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，模压成型 Shaw A, molded |
91 | ASTM D2240 | |
|
邵氏 D，模压成型 Shaw's D, molded |
50 | ASTM D2240 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
|||
|
2% 正割，TD，50 µm，吹塑薄膜 2% secant, TD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
2% 正割，MD，50 µm，吹塑薄膜 2% secant, MD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
|||
|
断裂，模压成型 Fracture, molded |
MPa | ASTM D638 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，模压成型 Fracture, molded |
% | ASTM D638 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Gardner Impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709-B | |
|
撕裂强度 tear strength |
|||
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 2 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.0 µm，吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
固乐科化学Gerphos阻燃剂：完满的阻燃处理方案
2017-05-03 德国固乐科化学将在Chinaplas 2017上展示一种新型聚氨酯超细纤维合成革用无卤阻燃剂，新型的Gerphos阻燃剂可承受聚氨酯超细纤维合成革受苛刻的生产条件。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付