牌号简介 About |
---|
Alkatane® HDF895是一种中等分子量高密度聚乙烯级,具有高硬度和优异的防潮性能。薄膜挤出:Alkatane® HDF895特别适用于生产用于干燥食品包装的薄膜,低水分传输可延长保质期。许多其他应用受益于混合Alkatane® HDF895以提高LDPE/LLDPE基薄膜的硬度,包括在高清晰度共挤薄膜的核心层。 Alkatane HDF895 is a medium molecular weight High Density Polyethylene grade with high stiffness and excellent moisture barrier properties. Film Extrusion: Alkatane HDF895 is particularly suitable for the production of film for the packaging of dry foods where low moisture transmission may allow extended shelf life. Numerous other applications benefit from blending Alkatane HDF895 to enhance the stiffness of LDPE / LLDPE based films, including in the core layer of high clarity coextruded films. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.962 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
18 | µm | |
割线模量 Secant modulus 2 |
|||
2% 正割,MD:18 µm 2% secant, MD: 18 µ m |
750 | MPa | |
2% 正割,TD:18 µm 2% secant, TD: 18 µ m |
780 | MPa | |
拉伸强度 tensile strength 3 |
|||
MD,屈服,18 µm MD, yield, 18 µ m |
MPa | ||
TD,屈服,18 µm TD, yield, 18 µ m |
MPa | ||
MD,断裂,18 µm MD, fracture, 18 µ m |
MPa | ||
TD,断裂,18 µm TD, fracture, 18 µ m |
MPa | ||
拉伸应变 Tensile strain 3 |
|||
MD,断裂,18 µm MD, fracture, 18 µ m |
% | ||
TD,断裂,18 µm TD, fracture, 18 µ m |
% | ||
落锤冲击 Gardner Impact 4 |
|||
18 µm 18 µm 4 |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
MD,18 µm MD,18 µm |
cN | ||
TD,18 µm TD,18 µm |
cN |
备注 |
---|
2、20 mm/min |
3、50 mm/min |
4、F50 |
【新闻资讯】查看全部 ![]()
海信集团换帅!周厚健卸任后,海信国际化仍然面临挑战
2022-03-14 2022年3月12日,海信集团控股有限公司(以下简称海信集团)原董事长周厚健宣布退休,主管海信海外业务的副董事长林澜将接任。 周厚健于1982年进入青岛电视机厂工作,十年后升任厂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |