牌号简介 About |
---|
MARCOBLEND 2000是一种阻燃的玻璃纤维增强聚碳酸酯树脂。该树脂无卤,符合TCO和RoHS认证。其独特的特点是加工性好、刚度好、尺寸稳定性好,适用于TFT液晶显示器框架和内部结构件。 MARCOBLEND 2000 is an ignition resistant and glass fiber reinforced polycarbonate resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
18 | g/10min | ASTM D1238 |
收缩率 Shrinkage |
|||
MD MD |
0.30 到 0.50 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
69.0 | MPa | ASTM D638 |
弯曲模量 Flexural Modulus |
3390 | MPa | ASTM D790 |
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Coeff.of linear therm expansion |
ASTM D696 | ||
MD MD |
1/℃ | ASTM D696 | |
TD TD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
凯柏胶宝:TPE用于婴幼儿的Babynator垫子,实现 "清洁饮食"
2021-06-24 搜料网资讯: 一家位于奥地利的初创公司为婴幼儿开发了一套 学习吃饭的产品,使饮食更加清洁,该公司将凯柏胶宝公司的Thermolast K TPE化合物用于该解决方案的主要组成部分。 Babyna |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |