牌号简介 About |
---|
与其他聚苯硫醚注塑成型化合物相比,Ryton® R-4-230NA和R-4-230BL 40%玻璃纤维增强聚苯硫醚化合物可减少闪光并提高加工性能。 Ryton® R-4-230NA and R-4-230BL 40% glass fiber reinforced polyphenylene sulfide compounds provide reduced flash and improved processability compared to other polyphenylene sulfide injection molding compounds. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.68 | g/cm³ | ASTM D792 |
收缩率 Shrinkage |
|||
TD:3.2 mm TD:3.2 mm |
0.50 | % | |
MD:3.2 mm MD:3.2 mm |
0.20 | % | |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
9.0 | kJ/m² | ISO 180/A |
3.2mm 3.2mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
kJ/m² | ISO 180 | |
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
TD TD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
导热系数 Thermal Conductivity |
W/m/K | ||
UL温度额定值 UL temperature rating |
℃ | UL 746B | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
25 ℃,1 kHz 25 ℃,1 kHz |
ASTM D150 | ||
25 ℃,1 MHz 25 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
25℃,1 kHz 25℃,1 kHz |
ASTM D150 | ||
25℃,1 MHz 25℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Comparative Tracking Index |
V | UL 746 | |
绝缘电阻 insulation resistance 2 |
|||
90℃ 90℃ 2 |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
极限氧指数 Oxygen Index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
弯曲模量 Flexural Modulus |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
|||
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 95%RH, 48 hr |
【新闻资讯】查看全部 ![]()
中国奥美凯成为高新技术企业
2017-04-12 奥美凯聚合物(苏州)有限公司,现已被中国政府授予“高新技术企业”的荣誉!在未来的三年里,奥美凯将为此殊荣继续做出努力。奥美凯是一家专门为聚合物产品客户提供定制化颜色、添加剂解决方案和改性工程塑料的全球性供应商。 奥美凯亚太区副总裁 / 董事总经理Stanley Teoh 说:“我们很自豪能够赢得这么高的荣誉,这积极反映了我们的中国员工在这段时间内做出的不懈努力。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |