Pocan T 7331 000000 PBT+PET,30%玻璃纤维,注塑,改善表面光洁度,提高温度峰值负荷 POCAN® T7331 000000 PBT+PET, 30 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® T7331 000000 PBT+PET, 30 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® T7331 000000 PBT+PET, 30 % glass fibers, injection molding, improved surface finish, increased temperature peak load |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.80 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
30.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
ISO 294-4 | ||
TD:270℃,2.0 mm TD:270℃,2.0 mm |
0.90 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs |
0.20 | % | ISO 294-4 |
MD:270℃,2.0 mm MD:270℃,2.0 mm |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs |
% | ISO 294-4 | |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿能量 Membrane puncture energy |
J | ISO 6603-2 | |
膜刺穿力 Membrane puncture force |
N | ISO 6603-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temperature |
|||
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
220℃ 220℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能 ELECTRICAL |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
Halving Interval Halving Interval |
IEC 60216 | ||
-- -- |
℃ | IEC 60216 | |
-- -- |
℃ | IEC 60216 | |
温度指数 Temperature index |
IEC 60216 | ||
介电强度 Dielectric strength |
IEC 60216 | ||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
拉伸冲击强度 Tensile impact strength |
IEC 60216 | ||
拉伸强度 tensile strength |
IEC 60216 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
阻燃等级 Flame Class Rating |
ISO 3795 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
ISO Shortname ISO Shortname |
ISO 7792 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲强度 Flexural Strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲应变 Flexural Strain |
% | ||
球压硬度 ball-indentation hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 90°C MT, 600 bar |
3 60x60x2; MT 90°C; 600 Bar |
4 60x60x2 |
5 60x60x2mm |
6 0,079 in/min |
7 2 mm/min |
8 Pull Rate: 2 mm/min; 50% RH |
9 23°C |
10 10°C/min |
11 Tensile Impact Strength |
12 Electric Strength |
13 Tensile Strength |
14 20000 h |
15 程序 A |
16 US-FMVSS302 |
【新闻资讯】查看全部 ![]()
国常会重磅定调,做好生活必需品保供稳价!看十大关键表述
2021-11-04 搜料网资讯: 据央视网,国务院总理李克强11月2日主持召开国务院常务会议,听取国务院第八次大督查情况汇报,要求围绕市场主体需求、群众关切和用好政府资金抓实工作;审议通过 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |