牌号简介 About |
---|
说明:SEB853是一种采用高压技术生产的低密度聚乙烯。用该产品获得的薄膜表现出优异的光学性能、良好的密封性和低凝胶含量。不含添加剂。该等级的最低生物基含量为95%,根据ASTM D6866测定。应用:典型的吹塑薄膜应用包括尿布和其他一般用途的薄膜,以及LLDPE和HDPE混合物。工艺:吹塑和铸膜挤出 Braskem PE SEB853 SEB853 is a low density polyethylene produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: Typical blown film applications include films for diapers and other general purposes as well as LLDPE and HDPE blends. Process: Blown and Cast Film Extrusion Braskem PE SEB853 SEB853 is a low density polyethylene produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: Typical blown film applications include films for diapers and other general purposes as well as LLDPE and HDPE blends. Process: Blown and Cast Film Extrusion Braskem PE SEB853 SEB853 is a low density polyethylene produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: Typical blown film applications include films for diapers and other general purposes as well as LLDPE and HDPE blends. Process: Blown and Cast Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.7 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
95 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Gardner Impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,38.0 µm,吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部 ![]()
杜邦™ TYVEK® 40L 医疗包�b资料全球首发
2017-09-26 2017年是杜邦™ Tyvek® 特卫强® 品牌诞生50周年。值此之际,杜邦™ Tyvek® 于2017年9月20日在MEDTEC 2017(第十三届国际医疗器械设计与制造技术展览会)上全球首发最新的Tyvek® 40L 医疗包�b材料。这款针对医疗包装应用的全新规格Tyvek® 材料,旨在为较轻重量和较低风险的医疗器械提供更经济有效的包�b选择。杜邦™ Tyvek® / Typar® 全球业务总监Christian Marx、Tyvek® 医疗包装全球业务总监Margaret Pyers |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |