| 牌号简介 About |
|---|
| Fortron® 1130L4 FC是一种30%玻璃纤维增强PPS，具有优异的耐热性和耐化学性，可用于食品接触应用。它本身具有阻燃性，硬度高，强度和刚度平衡良好。特别适用于需要较长流动长度的薄壁零件。由于填料含量低，该等级在二次操作中也表现出良好的可焊性。 Fortron 1130L4FC is a 30% glass-reinforced PPS that has excellent heat and chemical resistance for use in food contact applications. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content. |
产品描述 Product Description
用途：非特定食品应用;薄壁部件;
性能特点： 防火阻燃等级V-0; 焊接; 机械强度好; 耐化学性; 耐高温; 硬度高; 阻燃; 食品接触; Good Rigidity,Good Hardness,Flame Characteristics,Food contact compliance,High Heat Resistance,Solvent resistance,Welding,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
|||
|
-- -- |
1.60 | g/cm³ | ASTM D792 |
|
-- -- |
1.58 | g/cm³ | ISO 1183 |
|
特定体积 Specific volume |
0.636 | cm³/g | ASTM D792 |
|
收缩率 Shrinkage |
|||
|
MD MD |
0.30 到 0.50 | % | ASTM D955 |
|
TD TD |
0.60 到 0.90 | % | ASTM D955 |
|
TD TD |
% | ISO 294-4 | |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water Absorption |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
玻璃化转变温度 Glass transition temperature 3 |
℃ | ISO 11357-2 | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
ISO 11359-2 | ||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
TD TD |
1/℃ | ISO 11359-2 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
|||
|
-- -- |
ohms·cm | ASTM D257 | |
|
-- -- |
ohms·cm | IEC 60093 | |
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
1 kHz 1 kHz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Comparative Tracking Index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Specimen Thickness（Shrinkage） Specimen Thickness（Shrinkage） |
mm | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
M 级 M-level |
ISO 2039-2 | ||
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Flexural Modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 Flexural Strength 2 |
MPa | ISO 178 | |
| 备注 |
|---|
| 2 Break |
| 3 10°C/min |
|
【新闻资讯】查看全部 
俄罗斯北溪2号设施下周将试运行，为德国的天然气运输做准备
2021-06-12 搜料网资讯： 6月2日，列宁格勒地区的北溪2号设施将于下周开始测试，为德国的天然气运输做准备工作。列宁格勒州州长亚历山大德罗兹登科星期三在参加。 德罗兹登科在参加圣彼得堡 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付