| 牌号简介 About |
|---|
| Paryls PSU F3250GL20颗粒以内衬铝箔袋的纸箱提供，如果包装未受损，可以无限期储存。Paryls PSU F3250GL20颗粒吸收水分非常迅速。因此，在加工前，颗粒需要在真空或干燥空气干燥器中在160℃下干燥至少6h。特点Paryls PSU F3250GL20，树脂是一种20%玻璃纤维增强聚砜（PSU）。玻璃纤维大大提高了聚砜树脂的刚性、拉伸强度、抗蠕变、尺寸稳定性和耐化学性。高性能使这些树脂在许多工程应用中成为金属的有效替代品。 PARYLS® PSU F3250GL20 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PSU F3250GL20 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 160 °C in a vacuum or dry air drier prior to processing. Features PARYLS® PSU F3250GL20, resin is a 20% glass fiber reinforced polysulfone(PSU). Glass fiber substantially increasee the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties make these resins particularly effective alternatives to metals in many engineering applications. |
产品描述 Product Description
颜色：自然色,黑色,灰色
加工条件：挤出 Extrusion
性能特点： 防火阻燃等级V-0; 防火阻燃等级HB; 机械强度好; 尺寸稳定性好; 耐化学性; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,Solvent resistance,HB,V-0
填料：玻璃纤维 20
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.38 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
343℃，2.16kg 343℃，2.16kg |
5.0 到 10 | g/10min | ISO 1133 |
|
收缩率 Shrinkage |
ISO 294-4 , ISO 2577 | ||
|
TD TD |
0.50 | % | ISO 294-4，ISO 2577 |
|
MD MD |
0.30 | % | ISO 294-4，ISO 2577 |
|
吸水率 Water Absorption |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.20 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Flexural Modulus |
MPa | ISO 178 | |
|
弯曲强度 Flexural Strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
kJ/m² | ISO 180/A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
玻璃化转变温度 Glass transition temperature 2 |
℃ | ISO 11357-2 , DSC | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
|||
|
MD：23℃ MD：23℃ |
1/℃ | ISO 11359-2 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity 3 |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity 3 |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength 4 |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Comparative Tracking Index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
4.50 mm 4.50 mm |
UL 94 | ||
| 备注 |
|---|
| 2 10°C/min |
| 3 100V |
| 4 K20/K20, (60*60*1 mm³) |
|
【新闻资讯】查看全部
陶氏杜邦芳纶中间体将在印度投产
2018-03-15 陶氏杜邦计划外包给印度一条芳纶中间体生产线，用于其防弹Kevlar面料和阻燃Nomex材料。新泽西州工厂关闭将导致100个岗位失业，投资5000万美元进行现代化改造的弗吉尼亚州将继续生产。 新泽西州工厂将于本月结束生产活动，该生产线将于今年夏季解体。当地报道称，下岗人员可能将被转移到其他陶氏杜邦工厂。 特拉华新闻评论称，由于未来数月的分裂，印度Transpek公司将成为美国市场未来的主要供应商。 一位发言人向报社表示“从其他拥有更新，更具成本 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付