| 牌号简介 About |
|---|
| Adiprene M 3900是一种聚碳酸酯基MDI端接液体聚氨酯预聚物。这种新的预聚物具有独特的耐热老化和抗水解性能。当与1，4丁二醇固化，这一成员的ADIPRENE家族生产高质量的硫化胶，硬度为96肖氏A。该产品的特点是：撕裂强度高，耐磨性好，耐溶剂性好，在加工温度下耐水解性好，使用寿命适合机器和手工配料。 ADIPRENE M 3900 is a polycarbonate - based, MDI-terminated liquid urethane prepolymer. This new prepolymer is unique in its resistance to heat aging and hydrolysis. When cured with 1,4 Butanediol, this member of the Adiprene family produces high quality vulcanizates that are 96 Shore A in hardness. The features of ADIPRENE M 3900 include: High Tear Strength Excellent Abrasion resistance Good Solvent Resistance Good Hydrolysis Resistance Adiprene M3900 at processing temperature has a working life suitable for both machine and hand-batching procedures. |
产品描述 Product Description
性能特点： 耐磨; 机械强度好-撕裂; 耐化学性; 耐水解; 耐老化; Good heat aging resistance,Hydrolysis stability,Good tear strength,Good wear resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
38.7 | MPa | ASTM D412 |
|
100% 应变 100% strain |
15.3 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
260 | % | ASTM D412 |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
111 | kN/m | ASTM D624 |
|
开裂 cracking |
23 | kN/m | ASTM D470 |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
储存稳定性 storage stability |
min | ||
|
后固化时间 Post curing time |
|||
|
115℃ 115℃ |
hr | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
115℃ 115℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
压缩强度 compressive strength |
ASTM D695 | ||
|
5% 应变 5% strain |
MPa | ASTM D695 | |
|
10% 应变 10% strain |
MPa | ASTM D695 | |
|
15% 应变 15% strain |
MPa | ASTM D695 | |
|
20% 应变 20% strain |
MPa | ASTM D695 | |
|
25% 应变 25% strain |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部
英力士美国乙烯工厂方案扩能
2016-03-24 英力士集团正考虑利用美国低廉的天然气液体原料在美国扩大生产乙烯。 英力士美国烯烃&聚合物CEO Dennis Seith称该公司位于美国休斯敦南部Chocolate Bayou的乙烯工厂年产能可能会增加250,000Ktpa，另外该工厂还会新增部分聚丙烯和混合烯烃产能。今年内将就这三项投资作出最终决策，新增乙烯最终会在下一个十年内投入使用。 美国本土丰富的页岩气使美国成为生产乙烯成本最为低廉的国家之一，而乙烯是最常用到的石化产品之一，其派生产品如聚乙 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付