牌号简介 About |
---|
聚苯乙烯冲击8260是一种高冲击聚苯乙烯挤出和注射应用。与标准高冲击等级相比,该等级具有更好的抗环境应力开裂性能。该产品专门设计用于生产冰箱部件:内衬、门内衬、注入部件等。该等级也适用于生产可能导致应力开裂的产品,如脂肪、油……聚苯乙烯冲击8260在低温下保持了良好的机械性能,使该等级适合于冷冻包装;它还提供了良好的印刷性能。热成型应用表,冰箱内衬,低温包装应用(冰淇淋盒和盖子),腐蚀性食品包装,亚光处理,软接触。 POLYSTYRENE IMPACT 8260 is an high impact polystyrene for extrusioin and injection applications. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. The product has been specifically designed for the production of refrigerator part: inner liners, door liners, injected parts etc. This grade is also proposed for the production of packaging intended for products likely to cause stress cracking e.g. fats, oil... POLYSTYRENE IMPACT 8260 retains good mechanical properties at low temperatures making this grade suitable for frozen packaging; it also affords good printing performance. Applications Sheet for thermoforming, fridges liners, low temperature packaging applications (ice cream boxes and lids), packaging for aggressive foodstuffs, matt finish, soft touch. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.60 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
2.8 | g/10min | ASTM D1238 |
收缩率 Shrinkage |
0.40 到 0.70 | % | ISO 294-4 |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
介电强度 Dielectric strength |
|||
23℃ 23℃ |
kV/mm | IEC 60243-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
伊士曼延续第四年获评“全球最具商业品德企业”
2017-03-17 日前,伊士曼(Eastman)宣布连续第四年被美国道德村协会(Ethisphere Institute)评为“全球最具商业道德企业”。这一权威榜单嘉奖了伊士曼长期以来在引领商业道德最高标准和实践方面所作出的努力。 “在伊士曼,我们知道要获得成功,必须与利益相关者建立信任和信心。”伊士曼董事长兼首席执行官Mark Costa表示,“伊士曼整个团队致力于将诚实与诚信的经营准则应用于日常实践,从而再度获得这一殊荣,我对此深感自豪。” “我们的目标是致力于切实提高人 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |