| 牌号简介 About |
|---|
| BaydUR 646是一种用于反应注射成型（RIM）工艺的硬质聚氨酯结构发泡体系。该系统作为两种反应性液体成分提供：组分A是聚合物二苯甲烷二异氰酸酯（PMDI），组分B是不含CFC-或HCFC发泡添加剂的配方多元醇系统。BaydUR 646系统用于生产复合材料的泡沫芯，例如滑水板、尾板、雪板以及运输和海洋市场的各种部件。与任何产品一样，在给定应用中使用Baydur 646系统必须由用户提前进行测试（包括现场测试等），以确定适用性。 Baydur 646 is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components: Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The Baydur 646 system is used to produce foam cores for composite applications, such as water skis, wake boards, snow boards, and various components for the transportation and marine markets. As with any product, use of the Baydur 646 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
产品描述 Product Description
用途：汽车领域的应用;结构泡沫;体育用品;船舶应用;
加工条件：反应注射成型 (RIM)
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.479 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage |
|||
|
MD：6.35 mm MD：6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
内部方法 | ||
|
-- -- 2 |
8.8 | kJ/m² | 内部方法 |
|
-- -- 3 |
9.0 | kJ/m² | 内部方法 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热固组件 Thermosetting components |
|||
|
部件 A Component A |
按重量计算的混合比: 110 | ||
|
部件 B Component B |
|||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 D，6.35 mm Shaw D, 6.35 mm |
ASTM D2240 | ||
|
邵氏 D，12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
断裂，6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
|
断裂，12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
ASTM D638 | ||
|
断裂，6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
|
断裂，12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus |
ASTM D790 | ||
|
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
|
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength |
ASTM D790 | ||
|
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
|
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
ASTM D695 | ||
|
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
|
12.7 mm 12.7 mm |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.5 |
| 3 0.25 in |
|
【新闻资讯】查看全部
超耐寒塑料初次在俄罗斯研制出
2018-07-04 俄媒称，莫斯科国立科技大学的专家研制出可在不低于零下80摄氏度的严寒中使用的耐摩擦聚合材料。在北极大规模开采矿物需要复杂的工业设备和有大量摩擦单元的重型装备。在雅库特的所谓寒极地带曾经记录过零下67摄氏度的低温。 据俄罗斯《消息报》网站7月2日报道，北极的气候条件对设备的稳定性提出了苛刻的要求。在交通不便的情况下，一旦机械轴承因经受不住严寒而损坏，就可能意味着重大经济损失。对开采机构来说，在机器中使用能够长期经受非标准环境考验的可活动部件至关重要。 报道称， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |