牌号简介 About |
---|
Petra® 130是一种30%玻璃纤维增强聚对苯二甲酸乙二醇酯注塑成型化合物。它有天然和色素版本。它表现出优异的综合性能,包括高温下的高强度和刚度,具有良好的耐化学性和尺寸稳定性。应用Petra® 130通常推荐用于汽车门锁部件、外壳、齿轮和电气和机械部件等应用。 Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate injection molding compound. It is available in natural and pigmented versions. It exhibits a superb combination of performance properties including high strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability. Applications Petra 130 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | ASTM D792 |
密度 Density |
1.55 | g/cm³ | ISO 1183 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.40 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
9.0 | kJ/m² | ISO 179 |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
95 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 ELECTRICAL |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
1.5 mm 1.5 mm 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
-40℃ -40℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
80℃ 80℃ |
MPa | ISO 527-2 | |
120℃ 120℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ASTM D638 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ASTM D638 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
断裂,121℃ Fracture, 121 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
ASTM D790 | ||
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
ASTM D790 | ||
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部 ![]()
美元走强英国疫情反扑 美油一度跌逾3%失守70关口
2021-06-18 搜料网资讯: 周四(6月17日)美油自近2年来高位一度跌逾3%,至69.77美元/桶,后随着美股反弹,尾盘回升至71.06美元/桶。英国政府数据显示,周四该国单日新增病例数为11007例,创2月 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |