| 牌号简介 About |
|---|
| HIPTEN® 21018A6是为生产薄膜而开发的低密度聚乙烯树脂。HIPTEN® 21018A6具有优异的光学性能和良好的机械性能、良好的加工性和热密封性。添加了防滑剂和防堵剂，所得薄膜具有良好的防滑和防堵性能。HIPTEN® 21018A6净度高，适用于各种货物的包装。HIPTEN® 21018A6持有塞尔维亚卫生防护研究所颁发的健康证书。此外，还有符合性声明，声明产品符合拟接触食品的材料的欧洲规范。符合性声明由斯洛文尼亚Maribor公共卫生研究所发布。 HIPTEN® 21018A6 is low density polyethylene resin developed for production of thin blown film. HIPTEN® 21018A6 has extraordinary optical properties and very good mechanical properties, good processability and heat sealability. The addition of slip and antiblock agents results in good sliding and antiblocking properties of produced film. HIPTEN® 21018A6 has high clarity and is suitable for packaging for a wide variety of goods. HIPTEN® 21018A6 has Health Certificate issued by Institute for Health Protection of Serbia. Also, has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
产品描述 Product Description
用途：薄膜;包装;袋子;
加工条件：吹塑薄膜
性能特点： 抗结块性; 可回收; 高光滑性; 透光性好; 光学性能; 热封性好; 易加工; Excellent Processability,Good Clarity,Good heat sealing,Smoothness,Renewable resources,Optical performance,High anti-blocking
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.921 | g/cm³ | ISO 1183/D |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 | µm | |
|
拉伸强度 tensile strength |
ISO 1184 | ||
|
TD，屈服，40 µm TD, yield, 40 µ m |
10.0 | MPa | ISO 1184 |
|
MD，断裂，40 µm MD, fracture, 40 µ m |
23.0 | MPa | ISO 1184 |
|
TD，断裂，40 µm TD, fracture, 40 µ m |
MPa | ISO 1184 | |
|
拉伸应变 Tensile strain |
ISO 1184 | ||
|
断裂 fracture |
% | ISO 527-2 | |
|
MD，断裂，40 µm MD, fracture, 40 µ m |
% | ISO 1184 | |
|
TD，断裂，40 µm TD, fracture, 40 µ m |
% | ISO 1184 | |
|
落锤冲击 Gardner Impact |
|||
|
40 µm 40 µm |
g | ASTM D1709-A | |
|
撕裂强度 tear strength 2 |
ASTM D1922 | ||
|
MD，40 µm MD，40 µm |
kN/m | ASTM D1922 | |
|
TD，40 µm TD，40 µm |
kN/m | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
屈服 yield |
MPa | ISO 527-2 | |
|
断裂 fracture |
MPa | ISO 527-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Blown Film |
|
【新闻资讯】查看全部 
模具的分型面选取时要留意什么？
2018-01-02 塑料在模具型腔凝固形成塑件为了将其取出来必须将型腔打开，也就是必须将模具分成两个部分即定模和动模两部分，这两部分接触的面成为分型面。 分型面的选取时要注意问题如下： |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付