牌号简介 About |
---|
DINALEN® 35是含有添加剂的低密度聚乙烯。它主要用于吹膜挤出,而其他加工技术可用于较小程度。DINALEN® 35的拉伸性能非常好,拉伸膜的刚度、机械性能和光学性能平衡良好。DINALEN® 35在推荐的熔融温度范围165°C到185°C之间挤压。推荐的薄膜厚度:0.030 mm到0.100 mm。 DINALEN® 35 is low density polyethylene containing additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 35 exhibits excellent very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 35 is extruded at recommended melt temperature range between 165°C and 185°C. Recommended film thickness: 0.030 mm to 0.100 mm. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
薄膜厚度 film thickness |
0.03 mm to 0.100 mm | ||
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
23.0 | MPa | ISO 527-3/500 |
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
断裂,模压成型 Fracture, molded |
% | ISO 527-2/200 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3/500 | |
落锤冲击 Gardner Impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ISO 7765-1 | |
裤型撕裂耐性 Pant tear resistance 2 |
ISO 6383-1 | ||
MD:50 µm,吹塑薄膜 MD: 50 µ m, blow molded film |
N/mm | ISO 6383-1 | |
TD:50 µm,吹塑薄膜 TD: 50 µ m, blow molded film |
N/mm | ISO 6383-1 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,50 µm,吹塑薄膜 20 °, 50 µ m, blow molded film |
|||
60°,50.0 µm,吹塑薄膜 60 °, 50.0 µ m, blow molded film |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
MPa | ISO 527-2/200 | |
拉伸强度 tensile strength |
ISO 527-2/200 | ||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2/200 | |
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2/200 | |
摩擦系数 Frictional coefficient |
ISO 8295 | ||
与自身 - 动态 With oneself - dynamic |
ISO 8295 | ||
与自身 - 静态 With oneself - static |
ISO 8295 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 7.9 in/min |
【新闻资讯】查看全部 ![]()
江苏特铄:同舟十载 筑梦未来
2021-05-05 搜料网资讯: 十年回首往昔,感慨万千; 十年辛勤耕耘,硕果累累! 十年弹指一挥间,江苏特铄工程材料科技有限公司(以下简称江苏特铄),从一个默默无闻的小公司,如今发展壮大成为 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |