Aristech Acrylics LLC Acrysteel IMA是一种连续铸造的抗冲击丙烯酸板,一面具有哑光饰面和溶剂粘合性。使用0.125”(3.17 mm)厚透明Aristech压克力有限责任公司Acrysteel IMA压克力板测定以下物理性能。其他厚度和/或颜色(半透明或不透明)的属性可能有所不同。 Aristech Acrylics LLC Acrysteel® IMA is a continuous cast impact acrylic sheet with a matte finish on one side and solvent cementability. The following physical properties were determined using 0.125" (3.17 mm) thickness clear Aristech Acrylics LLC Acrysteel® IMA acrylic sheet. Properties may vary somewhat on other thicknesses and/or colors (translucent or opaque). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 3 |
1.17 | g/cm³ | ASTM D792 |
吸水率 Water Absorption |
|||
饱和,3.18 mm Saturation, 3.18 mm |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
3.18 mm 3.18 mm |
587 | J/m | ASTM D6110 |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
3.2mm 3.2mm |
43 | J/m | ASTM D256-A |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 4 |
|||
4.75 mm 4.75 mm 4 |
21.7 | J | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
导热系数 Thermal Conductivity 3 |
W/m/K | 内部方法 | |
热稳定性 thermal stability 5 |
|||
180℃,3.18 mm 180℃,3.18 mm 5 |
ASTM D4802 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
3.20 mm 3.20 mm |
UL 94 | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 3 |
ASTM D542 | ||
透光率 Light Transmission |
|||
3180 µm 3180 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
ASTM D1925 | ||
3.18 mm 3.18 mm |
YI | ASTM D1925 | |
4.75 mm 4.75 mm |
YI | ASTM D1925 | |
5.59 mm 5.59 mm |
YI | ASTM D1925 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热成型温度 Hot forming temperature |
|||
3.18 mm 3.18 mm |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级,3.18 mm M-grade, 3.18 mm |
ASTM D785 | ||
巴氏硬度 Babbitt hardness |
|||
3.18 mm 3.18 mm |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,3.18 mm Yield, 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.125 in |
3 FTMS 406-M-1074 |
4 30 min |
【新闻资讯】查看全部
我国中小型塑料企业现状:夹缝中求生活
2016-05-04 众所周知,我国是世界主要的塑料大国。目前,国内废塑料加工企业总共有3000多家,进口废塑料加工企业也有1400家之余。国内废塑料产生量为3292万吨,进口加工利用企业主要集中在东北沿海地区,主要以广东,浙江、福建为主。不过最近这两年,随着建筑行业增速放缓,经济下行压力增大,塑料行业受到影响,尤其是一些中小塑料加工企业,随着经济环境的改变,开始在夹缝中求生存。 我国中小型塑料企业现状:夹缝中求生存 现如今,塑料加工企业不好做,主要是缺乏创新意识。现在很多塑料加 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |