| 牌号简介 About |
|---|
| EMERGE™ PC/ABS 7700高级树脂是一种不含氯或溴添加剂的阻燃PC/ABS混合物。它具有优越的可加工性，适用于注塑成型应用。这一等级具有良好的美学，是紫外线稳定，可定制颜色。主要特性：根据ISO 10993（第5和10部分）测试应用：医疗设备外壳消费电子信息技术设备 EMERGE™ PC/ABS 7700 Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Main Characteristics: Tested under ISO 10993 (Parts 5 & 10) RoHS Compliant Applications: Medical equipment housings Consumer Electronics Information technology equipment |
产品描述 Product Description
用途：电器外壳;医疗/护理用品;电气/电子应用领域;外壳;
颜色：可用颜色
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 防火阻燃等级5VB; 阻燃; 防火阻燃等级5VA; 冲击性能好; 表面光泽度好; 耐候抗UV; 易加工; Weather resistance is good,Excellent Processability,Good surface appearance,High impact resistance,Halogen free,Flame Characteristics,V-0,5VA,5VB
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.17 | g/cm³ | ASTM D792 |
|
密度 Density |
1.18 | g/cm³ | ISO 1183/B |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
11 | g/10min | ASTM D1238 |
|
240℃，5.0kg 240℃，5.0kg |
20 | g/10min | ASTM D1238 |
|
260℃，2.16kg 260℃，2.16kg |
13 | g/10min | ISO 1133 |
|
收缩率 Shrinkage |
|||
|
MD MD |
% | ISO 294-4 | |
|
MD MD |
% | ASTM D955 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃，注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
|
23℃，注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
|
-18℃，3.2mm，注塑成型 -18 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
|
-7℃ -7℃ |
J/m | ASTM D256 | |
|
23℃，3.2mm，注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ISO 180/A | ||
|
-30℃，注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 180-A | |
|
23℃，注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 2 | |
|
维卡软化温度 Vicat Softening Temperature |
|||
|
-- -- |
℃ | ISO 306/A120 | |
|
B50 B50 |
℃ | ISO 306 | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM D696 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM D696 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
IEC 60243-1 | ||
|
1.6 mm，在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating 3 |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
2.00 mm 2.00 mm |
UL 94 | ||
|
2.50 mm 2.50 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
IEC 60695-2-12 | ||
|
1.5 mm 1.5 mm 3 |
℃ | IEC 60695-2-12 | |
|
2.0 mm 2.0 mm 3 |
℃ | IEC 60695-2-12 | |
|
2.5 mm 2.5 mm |
℃ | IEC 60695-2-12 | |
|
3.0 mm 3.0 mm 3 |
℃ | IEC 60695-2-12 | |
|
极限氧指数 Oxygen Index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
4 mm，注塑成型 4 mm, injection molded |
MPa | ISO 527-1-2 | |
|
3.20 mm，注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂，4 mm，注塑成型 Fracture, 4 mm, injection molded |
MPa | ISO 527-2/50 | |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ASTM D638 | |
|
屈服，4 mm，注塑成型 Yield, 4 mm, injection molding |
MPa | ISO 527-2/50 | |
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，4 mm，注塑成型 Fracture, 4 mm, injection molded |
% | ISO 527-2/50 | |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
|
屈服，4 mm，注塑成型 Yield, 4 mm, injection molding |
% | ISO 527-2/50 | |
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级，3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 标准 B (120°C/h), 压 力1 (10N) |
| 3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
| 4 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
|
【新闻资讯】查看全部 
沧州大化20万吨/年双酚A项目全面开工最新进展！
2021-05-04 搜料网资讯： 经过项目部近4个多月的努力，由赛鼎工程有限公司EPCM总承包的沧州大化20万吨/年双酚A项目以及配套公用工程和辅助设施于2021年4月初全面开工。目前，综合罐区、原料罐 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付