公司信息及水印






牌号简介 About |
---|
TN2006是一种乙烯-醋酸乙烯酯(EVA)共聚物,具有良好的力学性能、较高的柔韧性和韧性,即使在低温下也具有优异的光学和可销售性。此外,该产品具有良好的水蒸气阻隔性。熔融特性使管状薄膜设备具有可加工性,能够与许多其他材料一起共挤。 TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even at low temperatures. It has excellent optical and heat sealability properties. Additionally, this product has good water vapor barrier. The rheological properties allow processability in tubular film extrusion equipment, being able to be coextruded in combination with many other materials. Additives Antioxidant Application: Heat seal layer in coextruded and laminated films. Food packaging. Hood stretch films. Base polymer for agricultural films. Geomembranes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
18.0 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,模压成型 Shaw A, molded |
89 | ASTM D2240 | |
邵氏 D,模压成型 Shaw's D, molded |
39 | ASTM D2240 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
2% 正割,TD,50 µm,吹塑薄膜 2% secant, TD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
2% 正割,MD,50 µm,吹塑薄膜 2% secant, MD, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Gardner Impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709-B | |
撕裂强度 tear strength |
|||
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
g | ASTM D1922 | |
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 2 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部 ![]()
国内首批能化期权——PTA、甲醇期权在郑商所上市
2021-04-18 搜料网资讯: PTA、甲醇期权12月16日在郑州商品交易所(以下简称郑商所)上市交易。 PTA、甲醇期权是首批上市的能源化工期权品种。目前,PTA期货已经实现国际化,甲醇期货也将积极启动 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |