牌号简介 About |
---|
PR-1051I是一种高分子酚醛三聚氰胺改性酚醛树脂粉末。它通常用于摩擦,特别是离合器表面。性能:sumiliterisin pr-1051i是以三聚氰胺为改性剂的粉末酚醛树脂,具有良好的摩擦性能、良好的工艺性等生产摩擦的优点。含低六胺,分子量大,可减少热成型和后固化过程。中间三聚氰胺树脂改性。目的提高离合器片的硬度和抗振性能。 PR-1051 I is a High molecule novolak melamine modified phenolic resin powder. It is generally applied for friction especially for clutch facing. Characteristics SUMILITERESIN® PR-1051 I is powder novolak phenolic resin with melamine as modifier, have good friction properties, good process, and other merit in production of friction. It is including low hexamine that has high molecule number and hot molding and post curing process can be reduced. modified by middle melamine resin. It purpose to improve hardness and judder property in application of clutch facing. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Flow Length(125℃) Flow Length(125℃) |
1.00 到 3.00 | cm | |
颗粒大小分布 Particle size distribution |
|||
150μm 150μm |
< 5.0 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
93.0 到 113 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
胶凝时间 Gelation time |
|||
150℃ 150℃ |
0.33 到 0.67 | min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
北京理工大学发布阻燃新产品新技术
2017-08-09 北京理工大学材料学院近日召开了“国家阻燃材料工程技术研究中心”阻燃新产品新技术信息发布会。来自22家企业和机构的30位代表出席了发布会。 此次发布会上,“国家阻燃材料工程技术研究中心”的4位专家分别发布了8项阻燃剂和阻燃材料及相关技术,包括:高聚合度聚磷酸铵(APP结晶Ⅱ型)工业生产技术、阻燃剂纳米复合阻燃增效技术、膨胀型阻燃剂技术、阻燃聚氨酯硬泡用新型含氮聚醚多元醇合成技术、阻燃聚氨酯硬泡高效阻燃剂配方技术、阻燃聚氨酯硬泡白料制备技术、木器漆用羟基丙烯酸水性乳液中试生产技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |