| 牌号简介 About |
|---|
| 电积槽用乙烯基酯树脂美国11C是一种耐腐蚀的高分子量环氧乙烯基酯树脂。适用于制作整体式聚合物混凝土电解槽。性能好，用填料浸透，玻璃纤维风干；表面光滑致密，抗渗性好，力学性能优异，耐热性低，峰值放热低；厚部不开裂，低断面，柔韧性好，附着力强，适用于制备聚合物混凝土，特别是整体式电积混凝土。主要用于铜、锌、镍、钴等有色金属的湿法冶金行业。适用于真空输液过程。 Vinyl Ester Resin for Electrowinning Cell MERICAN-11C is a corrosion resistant epoxy vinyl ester resin with high molecular weight. It is suitable for making monolithic polymer concrete electrowinning cells. PROPERTY Good wet-out with fillers and glass fiber Air drying; Smooth and dense surface, good impermeability Excellent mechanical properties and heat resistance Low peak exothermic; Thick parts do not crack Low profile, good flexibility and strong adhesion APPLICATION Suitable for making polymer concrete, especially for monolithic electrowinning cells in copper, zinc, nickel, cobalt and other non-ferrous hydrometallurgy industry. Suitable for vacuum infusion process. |
产品描述 Product Description
用途：电气/电子应用领域;
颜色：黄色
加工条件：真空成型
性能特点： 低放热性; 耐腐蚀; 机械强度好-撕裂; 快速润湿; 耐化学性; 耐高温; 粘结性好; 高分子量; 韧性好; 耐碱; Good flexibility,Alkali resistant,Low Exotherm,Corrosion Resistant,High Heat Resistance,Good bond,High molecular weight,Good tear strength,Solvent resistance,Quick wetting
填料：玻璃纤维
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
酸值 acid value |
4.00 到 12.00 | mg KOH/g | |
|
固体含量 Solid content |
52 到 58 | % | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
95.0 到 105 | ℃ | ASTM D648 |
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
25℃ 25℃ |
150 到 250 | cP | |
|
胶凝时间 Gelation time |
|||
|
25℃ 25℃ 2 |
1.8 到 3.4 | hr | |
|
25℃ 25℃ 3 |
hr | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Gel to Peak Gel to Peak |
|||
|
-- -- 2 |
hr | ||
|
-- -- 3 |
hr | ||
|
放热峰值 exothermic peak |
|||
|
-- -- 2 |
℃ | ||
|
-- -- 3 |
℃ | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 1.5%Butanox M-50, 1.5%NL-49P (AkzoNobel) |
| 3 1.0%Butanox M-50, 1.0%NL-49P (AkzoNobel) |
|
【新闻资讯】查看全部
CTA溶剂交流技术装置在嘉兴石化再获使用
2019-01-08 继在汉邦(江阴)石化公司工业化应用取得成功后，由天华化工机械及自动化研究设计院有限公司自主研发设计制造的220万吨/年PTA装置CTA溶剂交换技术装置近日在嘉兴石化有限公司再获应用。 截至发稿时时，装置已稳定运行半年时间，其洗涤效率、醋酸损耗等关键技术指标和隔离块寿命等机械性能均优于BP-德国BHS设备性能，实现了弯道超车，打破了BP公司PTA技术一家独大的局面。 PTA装置CTA溶剂交换技术相比传统工艺优势明显：一套规模为220万吨的PTA装置生产每吨PT |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付