牌号简介 About |
---|
材料类型:黑色低粘度氟弹性体化合物,硬度邵氏A 65~75。基于含氟量很高的过氧化物固化氟弹性体,具有优异的耐化学品性能。特点:后固化时间短,铸模流动性好,脱模性好,不易发生闪蒸,具有优异的耐化学性:酒精、蒸汽、酸、化学品中含有胺。工艺方法:适用于压缩、转移、注射和挤出成型工艺。用途:用于化工、石化等行业的O型圈、垫片。实验室测试固化条件:压力固化:10分钟@170°C。烘箱:(1+4)小时@230°C Material Type: Black color low viscosity fluoroelastomer compound, hardness Shore A 65~75. Based on peroxide curable fluoroelastomer with very high fluorine content which brings outstanding chemicals resistance properties. Features: Short post cure time Excellent mold flow and mold release, resulting in less flash Extraordinary chemical resistance: Alcohol Fuel Steam Acids Chemicals containing amines. Process Methods: Suitable for compression, transfer, injection and extrusion molding processes. Applications: For O-rings, gaskets used in chemical and petrochemical industries. Lab Testing Curing Condition: Press Curing: 10min@170°C. Oven: (1+4)hrs@230°C |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.98 | g/cm³ | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
72 | ASTM D2240 | |
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
23.7 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
240 | % | ASTM D412 |
压缩形变 Compression deformation 2 |
|||
200℃,70 hr 200℃,70 hr 2 |
23 | % | ASTM D395 |
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 Change in Tensile Strength in Air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air |
|||
250℃,70 hr 250℃,70 hr |
% | ASTM D573 | |
空气中硬度计硬度的变化率 Change in Durometer Hardness in Air |
|||
250℃,70 hr 250℃,70 hr |
ASTM D573 | ||
拉伸强度的变化率 Change in Tensile Strength |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
极限伸长率的变化率 Change in Ultimate Elongation |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
邵氏硬度的变化率 Change rate of Shore hardness |
|||
23℃,70 hr,在基准燃料C中 23 ℃, 70 hr, in reference fuel C |
ASTM D471 | ||
体积变化 Volume change |
|||
23℃,70 hr,C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6 mm Buttons |
【新闻资讯】查看全部 ![]()
半导体涨价潮还能持续多久?当潮水退去,哪些公司在裸泳?
2021-12-21 搜料网资讯: 2021年,半导体行业经历了前所未有的缺货潮和涨价潮。其中,部分品种涨幅甚至超过300倍。二级市场方面,涨价潮所带来的红利早已兑现。市场普遍预期,缺货要到2022年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |