| 牌号简介 About |
|---|
| 警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。RTP 1100系列提供了强度、刚度、韧性、耐热性和优良电气性能的最佳平衡。它以极具竞争力的成本提供了良好的表面外观。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 1100 Series offers an optimum balance of strength, stiffness, toughness, heat resistance and excellent electricals. It offers good surface appearance at a very competitive cost. |
产品描述 Product Description
颜色：黑色,自然色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 机械强度好; 耐高温; 电气性好; 表面光泽度好; 韧性好; Good Rigidity,Good flexibility,Good surface appearance,Good Electrical Properties,High Heat Resistance,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage |
|||
|
MD：3.2 mm MD：3.2 mm |
0.20 | % | ASTM D955 |
|
吸水率 Water Absorption |
|||
|
23℃，24hr 23℃，24hr |
0.050 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
|
3.2mm 3.2mm |
75 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
|
3.2 mm 3.2 mm |
430 | J/m | ASTM D4812 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
导热系数 Thermal Conductivity |
W/m/K | ASTM C177 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
|||
|
1.59 mm 1.59 mm |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.60 mm 1.60 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength |
|||
|
屈服 yield |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
索尔维龙项目高功能含氟塑料消费线正式投产
2017-11-10 苏威特种聚合物(常熟)有限公司是比利时索尔维集团于2007年在新材料产业园投资建设的高端化学品和新材料企业，注册资本8533万美元，总投资2.53亿美元。目前，企业已投资建设三期项目，分别为一期总投资2300万美元的工程塑料超细粉末项目、二期总投资3500万美元的高分子复合材料项目和三期总投资1.95亿美元的龙项目。其中一期、二期项目均已竣工投产，三期龙项目中的氟橡胶部分已投产。聚偏氟乙烯，即高性能含氟塑料部分为本次竣工投产的生产线。2016年，公司实现产值3亿元，三期龙项目全部达产后预计 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付