| 牌号简介 About |
|---|
| ELITE™ 5401P增强聚乙烯树脂是一种通过陶氏原位技术生产的共聚物。它提供了一个独特的组合低密封启动，中等刚度和低阻塞的自动包装设备上的卓越性能。对于食品和特种包装薄膜，其优异的抗冲击性和撕裂性能，其优异的颜色稳定性符合：美国食品和药物管理局FCN 424欧盟，2011年第10号，详细信息请参考相关法规。 ELITE™ 5401P Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of low seal initiation, moderate stiffness and low blocking for excellent performance on automated packaging equipment. For food and specialty packaging films Superior impact resistance and tear properties Excellent color stability Complies with: U.S. FDA FCN 424 EU, No 10/2011 Consult the regulations for complete details. |
产品描述 Product Description
加工条件：吹塑薄膜
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
膜刺穿强度 Membrane puncture strength |
1.69 | J | 内部方法 |
|
膜刺穿力 Membrane puncture force |
35.6 | N | 内部方法 |
|
膜耐刺穿性 Membrane puncture resistance |
J/cm³ | 内部方法 | |
|
膜强度 Membrane strength |
ASTM D882 | ||
|
MD MD |
J/cm³ | ASTM D882 | |
|
TD TD |
J/cm³ | ASTM D882 | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD 1% secant, MD |
MPa | ASTM D882 | |
|
2% 正割，MD 2% secant, MD |
MPa | ASTM D882 | |
|
1% 正割，TD 1% secant, TD |
MPa | ASTM D882 | |
|
2% 正割，TD 2% secant, TD |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服 MD, yield |
MPa | ASTM D882 | |
|
TD，屈服 TD, yield |
MPa | ASTM D882 | |
|
MD，断裂 MD, fracture |
MPa | ASTM D882 | |
|
TD，断裂 TD, fracture |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂 MD, fracture |
% | ASTM D882 | |
|
TD，断裂 TD, fracture |
% | ASTM D882 | |
|
落锤冲击 Gardner Impact |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD MD |
g | ASTM D1922 | |
|
TD TD |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45° 45° |
ASTM D2457 | ||
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
厦门大学打通合成气制备乙二醇常压加氢催化技术难关
2022-04-16 厦门大学发布消息，4月15日，厦大谢素原院士、袁友珠教授团队在《科学》（ Science ）杂志上发表研究成果，首次将C 60 作为电子缓冲剂改性铜基催化剂，打通了从合成气制备乙二醇的 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付