| 牌号简介 About |
|---|
| 聚丙烯PPH 12020是一种澄清的高流动性均聚物，其熔体流动指数为60 g/10 min。聚丙烯PPH 12020的设计具有很高的刚度和出色的透明度。适用于透明包装的注塑成型。 Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning(94HB) and self-extinguishing grades(94V-0,V-2) exist, and electrical properties exhibited are the highest of any thermoplastic. Low water absorption is exhibited, and excellent electrical properties(CTI and GWIT) are retained over extended periods of usages, even with widely varied temperature and humidity conditions. The surface of molded products is smooth, and a low coefficient of friction is exhibited.As the amount of froction is low, PBT is suitable for use in application requiring friction and wear properties. The material is exceptionally reliable, with small in-use dimensional variation, and superior molding stability and dimensional precision. Long-term chemical resistance is exceptional, and at room temperature, there is almost no degradation in properties after. Both unreinforced and reinforced grades exhibit exceptional flowability, and excellent processability. Application:VCD drive frames Connectors Trimmers Switch buttons for gas-fired instantaneous water heaters Relay blocks Driers Rectifiers Outer handles Height sensor cases Door mirror stays Drive component housings Energy saving lamp. |
产品描述 Product Description
用途：包装;
颜色：清晰/透明
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 机械强度好; 均聚物; 透光性好; 流动性高; Good Rigidity,Good Clarity,High liquidity,Homopolymer,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.40 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage |
|||
|
MD MD |
1.4 到 2.0 | % | ASTM D955 |
|
吸水率 Water Absorption |
|||
|
23℃，24hr 23℃，24hr |
0.10 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
60.0 | MPa | ASTM D638 |
|
弯曲模量 Flexural Modulus |
5000 | MPa | ASTM D790 |
|
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
kJ/m² | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
kJ/m² | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
2 mm 2 mm |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
2 mm 2 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
【茂名石化】高熔高透聚丙烯树脂单月产量创历史新高
2020-10-23 搜料网资讯： 茂名石化高熔高透聚丙烯树脂单月产量突破1800吨，同比增幅约192%，创单月产量历史新高。 高熔高透共聚聚丙烯表现出流动性好、透明度高、析出少、刚韧平衡性好等优点 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |