牌号简介 About |
---|
Elastollan® 1185AW是一种基于聚醚的热塑性聚氨酯(TPU),含有增塑剂。它是专门为电线和电缆、薄膜和片材以及挤压成型应用而设计的。它含有非卤化阻燃剂,在0.75、1.5和3.0 mm壁厚的垂直火焰试验中,其额定值为UL-94V-2。它还通过了FAR 25.853(a)火焰测试。它具有优异的耐磨性、韧性、透明度、低温柔韧性、水解稳定性和抗真菌性。它具有优良的阻尼特性和优异的抗撕裂扩展性能。Elastcollan1185a以未着色的颗粒形式提供。 Elastollan® 1185AW is a polyether-based thermoplastic polyurethane (TPU) containing a plasticizer. It is specifically formulated for wire and cable, film and sheet, and extruded profile applications. It contains a non-halogenated flame retardant and is rated UL-94 V-2 in vertical flame test for wall thicknesses of 0.75, 1.5 and 3.0 mm. It also passes FAR 25.853 (A) flame test. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1185A is supplied uncolored in pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,3.80kg 190℃,3.80kg |
5.0 to 25 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
85 | ASTM D2240 | |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
19.3 | MPa | ASTM D412 |
弯曲模量 Flexural Modulus |
|||
注塑成型 injection molding |
20.7 | MPa | ASTM D790 |
泰伯耐磨性 Taber Abrasion |
mg | ASTM D1044 | |
Abrasion(DIN) Abrasion(DIN) |
mm³ | DIN 53516 | |
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
软化温度 Softening temperature |
|||
DMA DMA |
℃ | Internal Method | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部 ![]()
智能家居大范围普及 塑料光纤任重道远
2015-11-20 “通信市场需求不强烈,以大圣为例,我们的业务大多在工业控制、汽车、飞机及音响领域。”江西大圣塑料光纤有限公司总经理陈伟在接受记者采访时指出。塑料光纤通信技术符合国家“光进铜退”和低碳、节能、环保的产业发展方向,相信未来必将与石英光纤配合在宽带建设以及光纤到户的发展中担当举足轻重的角色,发挥“最后一百米”的关键性作用。然而,从目前的市场反馈情况来看,塑料光纤任重道远。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |