牌号简介 About |
---|
低烟、低毒、无卤、阻燃、硅烷交联化合物,用于所有类型电缆的低压绝缘和护套。这是一种低烟、低烟、阻燃的硅烷交联化合物,可作为热塑性塑料在高输出速率下加工,并在潮湿条件下固化后加工。接枝组分SX559与交联催化剂母粒CM540U混合,比例通常为95:5。该化合物结合了良好的机械、电气和阻燃性能,以满足包括BS7211在内的严格绝缘规范。该化合物还可用于需要高阻燃性的电缆的护套。 Low-smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for low voltage insulation and sheathing of all types of cable This is a low smoke, low fume, fire retardant silane crosslinkable compound which can be processed as a thermoplastic at high output rates and cured post processing by exposure to moisture. The graft component SX559 is mixed with a crosslinking catalyst masterbatch CM540U generally in the ratio 97:3 to 95:5 The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications including BS 7211. The compound can also be used for sheathing of cables requiring high fire retardance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | BS 2782 620A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.5 | g/10min | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
14.0 | MPa | IEC 60811-1-1 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
170 | % | IEC 60811-1-1 |
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 Change in Tensile Strength |
|||
135℃,168 hr 135℃,168 hr |
20 | % | IEC 60811-1-2 |
断裂时拉伸应力变化 Change in tensile stress during fracture |
|||
135℃,168 hr 135℃,168 hr |
% | IEC 60811-1-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
变形 deformation |
|||
100℃ 100℃ |
% | IEC 60811-3-1 | |
低温弯曲 Low temperature bending |
|||
-30℃ -30℃ |
IEC 60811-1-4 | ||
热固性 thermosetting 2 |
IEC 60811-2-1 | ||
负荷下伸长率:20 N/cm²,200℃ Elongation under load: 20 N/cm ², 200 ℃ |
% | IEC 60811-2-1 | |
冷却后最大永久伸长率 Maximum permanent elongation after cooling |
% | IEC 60811-2-1 | |
温度指数 Temperature index |
℃ | ISO 4589-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
绝缘电阻常数 - Ki Insulation resistance constant - Ki |
IEC 60502 | ||
20℃ 20℃ |
ohms·cm | IEC 60502 | |
90℃ 90℃ |
ohms·cm | IEC 60502 | |
传导率 Conductivity |
|||
of gases of gases |
µS/cm | IEC 60754-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
烟气中的腐蚀性气体 Corrosive gases in flue gas |
|||
pH pH |
IEC 60754-2 | ||
烟雾密度 Smoke density |
% | ASTM D2843 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Halogen Acid Gas Evolution Halogen Acid Gas Evolution |
% | IEC 60754-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cure assessment by hot set test (forced cured at 80°C in water) |
【新闻资讯】查看全部 ![]()
刚刚,中国恒大否认将破产重组!已公开三种兑付方案
2021-09-14 搜料网资讯: 2021年9月13日,恒大集团发表声明称,网络上近日出现的有关恒大破产重组的言论完全失实。公司目前确实遇到了前所未有的困难,但公司坚决履行企业主体责任,全力以赴 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |