牌号简介 About |
---|
符合ISO 1043-1的材料规范:30%长玻璃纤维增强聚丙烯共聚物。低排放。纤维与聚丙烯基体发生化学耦合。球是圆柱形的,通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene copolymer reinforced with 30weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
6200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
100 | MPa | ISO 527-2/1A/5 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
6000 | MPa | |
80℃ 80℃ |
MPa | ||
弯曲强度 Flexural Strength |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 ![]()
1月中国汽车销售280.9万辆 新动力汽车销量增4.3倍
2018-02-13 据中国汽车工业协会最新公布,2018年1月中国汽车产销量同比呈现两位数增长,大多数车型产销水平均高于上年同期。本月产销增速受工作日增加和政策变动影响较大。 统计显示,2018年1月,中国汽车产销分别完成268.8万辆和280.9万辆,环比分别下降11.6%和8.2%,同比分别增长13.6%和11.6%。 全国乘用车市场信息联席会预测,2018年中国车市增速将在4%,走势呈现前高后稳的态势,上半年增长仍总体较好。其中对于自主品牌而言,发展智能网联汽车将是自主品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |